洛氏硬度试验方法及其应用分析
摘要：论文通过洛氏硬度的试验方法及其应用分析，明确了Rockwell 574洛氏硬度计的试验方法、操作规程、应用范围及洛氏硬度的制样要求。对几种常见高温合金材料进行洛氏硬度分析，确定其在不同状态下所呈现的硬度值。
关键词：硬度 洛氏硬度 压头 表面粗糙度 变形痕迹 塑性变形 强度
ABSTRACT: Through the test method of Rockwell hardness and its application analysis, the test method, operation rules, application scope and sample preparation requirements of Rockwell 574 Rockwell hardness tester are defined. Rockwell hardness of several common superalloy materials was analyzed to determine their hardness values under different conditions.
Key words: hardness Rockwell hardness indenter surface roughness deformation trace plastic deformation strength
目 录
前言..............................................................................................3
第1章 洛氏硬度计........................................................................4
1.1 Rockwell 574洛氏硬度计目的.......................................................................4
1.2 洛氏硬度试验的基本原理..............................................................................4
1.3 洛氏硬度标尺及其应用范围..........................................................................6
1.4 洛氏硬度计配置..............................................................................................6
1.5 影响洛氏硬度值的因素..................................................................................8
第2章 R574洛氏硬度计操作规程..........................................11
2.1 范围................................................................................................................11
2.2 工作环境........................................................................................................11
2.3 试验前的准备工作........................................................................................11
2.4 硬度测试........................................................................................................11
2.5 硬度试验注意事项........................................................................................13
第3章 硬度检测样品要求.......................................................14
3.1 硬度检测样品一般要求................................................................................14
3.2 洛氏硬度制样要求........................................................................................15
第4章 洛氏硬度实例应用分析..................................................17
4.1 洛氏硬度计的验证........................................................................................17
4.2 GTD222洛氏硬度分析....................................................................................18
4.3 Mar-M-247洛氏硬度分析..............................................................................20
4.4 IN718洛氏硬度分析.......................................................................................22
4.5 3Cr13马氏体型不锈钢洛氏硬度分析............................................................25
第5章 金属表面洛氏硬度试验测量结果不确定度的评定........28
5.1 目的................................................................................................................28
5.2 仪器设备........................................................................................................28
5.3 原理................................................................................................................28
5.4 试验步骤........................................................................................................28
5.5 不确定评定....................................................................................................28
5.6 标准不确定分量的评定................................................................................29
5.7 合成标准的不确定度的评定........................................................................32
5.8 拓展不确定度的评定....................................................................................33
5.9 测量结果不确定度报告................................................................................33
六 结论：....................................................................................33
参考文献 .................................................................................. 34
七 小结......................................................................................34
前 言
金属的硬度是金属材料抵抗局部变形，特别是塑性变形、压痕或者划痕的能力，是衡量其软硬程度的指标。其检测设备简便，数据容易取得，因此具有很重要的代表性，故金属硬度检测成为常用的方法，深受许多科技、生产、教学、管理和企业人士所重视。新中国成立以来，我国重视与世界其他各国的往来，我们虚心向其他国家的学习先进的检测技术，因而在金属硬度检测方法的研究和相关标准的制定更引起重视，有了长足的发展。与国际比对结果说明，我国的金属硬度检测技术、检测标准已经达到了国际化的水平。相对于同一试样，选用不同的硬度测试方法测得的硬度值完全不同。我国已经有了布氏硬度、维氏硬度、洛氏硬度、里氏硬度、努氏硬度和肖氏硬度。然而在这几种常见的金属硬度试验方法中，洛氏硬度试验技术成熟、操作简便、应用范围广泛。
因此本篇文章将结合本人在某单位实验室从事力学性能检测的实习工作经历，对洛氏硬度进行系统的分析。目的是为了能够更加深入的了解洛氏硬度这种检测方法，以及为了以后能够更好的在实验室从事硬度检测工作。我们将通过日常工作试验、查阅有关书籍资料、国家相关标准、工作实践，对洛氏硬度的试验方法、试验设备、制样要求、实际操作规程及其应用进行分析。
参考文献：
[1] 计量测试技术手册编辑委员会.计量测试技术手册 第5卷 力学（二）【M】.中国计量出版社.1997.04
[2]周兆丰.测力硬度计量简明手册【M】.兵器工业部二九六区域力学计量站，北京.国防工业出版社.1987.08
[3]韩德伟.金属硬度检测技术手册【M】.中南大学出版社.2003.06
[4]李久林.金属硬度试验方法国家标准（HB、HV、HR、HL、HK、HS）实施指南【M】.中国标准出版社.2004.08
[5]邓星临、梁新邦.中国金属学会推荐技术和方法【M】.中国标准出版社.2006.09
[6]ASTM E18-2016【S】金属材料洛氏硬度标准测试方法
[7]GB/T 230.1-2018【S】中华人民共和国国家标准
[8]ISO 6508-1 第3版 2015-03-01【S】国际标准